摘要通过原位聚合的方法制备了三氧化二铝填充聚酰亚胺杂化薄膜。研究Al2O3的粒径、含量、分散处理方式及界面处理等对PI/ Al2O3杂化薄膜的力学性能和热-力学性能的影响。结果显示，随着Al2O3粒径的减小和含量的增加，杂化薄膜的弹性模量增大；而拉伸强度则随着Al2O3含量的增加先升高后降低，当Al2O3质量分数为5%时有最大值；对Al2O3进行超声波处理，可大幅提高聚酰亚胺杂化薄膜的拉伸强度和弹性模量；使用表活性剂KH550处理Al2O3，可明显提高聚酰亚胺杂化薄膜的拉伸强度和弹性模量。47387
The aluminum oxide filled polyimide composite films were prepared by in situ polymerization. The effect of the Al2O3 particle size, mass fraction, decentralized approach and interface processing on mechanical properties and thermal- mechanical properties of PI/Al2O3 films were studied; The results showed that with the Al2O3 particle size decreasing and mass fraction increasing, the elastic modulus of the composite film was increased; while with the mass fraction of Al2O3 increasing, its tensile strength increased first, then decreased; when Al2O3 mass fraction was 5wt%, the best value was emerged. To ultrasonic processing of Al2O3, PI composite membrane elastic modulus and tensile strength were improved greatly. Moreover, after adding the surface active agent KH550, PI composite membrane elastic modulus and tensile strength were improved.
毕业论文关键词：聚酰亚胺； 三氧化二铝； 性能
Keyword: polyimide；aluminum oxide ；performance
目录
第1章绪论 1
1.1 引言 1
1.2 聚酰亚胺的合成 1
1.2.1 一步合成法 1
1.2.2 二步合成法 1
1.2.3 三步合成法 2
1.2.4 气相沉积法 2
1.3 聚酰亚胺的改性 2
1.3.1 共混改性 2
1.3.2 主链引进柔顺性基团 2
1.3.3 引入功能化侧基 3
1.4 无机纳米粒子杂化聚酰亚胺的研制现状 3
1.4.1 Al2O3填充PI 3
1.4.2 SiO2填充PI 4
1.4.3 石墨烯填充PI 5
第2章 实验部分 6
2.1 实验原料及制备 6
2.1.1 原料 6
2.1.2 仪器设备 6
2.1.3 PI/Al2O3杂化薄膜的制备 6
2.1.4 测试 7
2.2 结果与讨论 7
2.2.1 Al2O3粒径对杂化薄膜力学性能的影响
-
PS-b-PHEMA及其双组分嵌段共...
-
PS-b-PNIPAM单组份及其双组份...
-
聚天青C/还原石墨烯杂化膜...
-
氧化锌/二氧化钛复合薄膜...
-
钙钆共掺杂氧化铈薄膜的制备及其表征
-
无极性ZnO薄膜的制备和表征研究
-
镍钙钐共掺杂氧化铈薄膜的制备工艺的研究
江苏省某高中学生体质现状的调查研究
C++最短路径算法研究和程序设计
NFC协议物理层的软件实现+文献综述
g-C3N4光催化剂的制备和光催化性能研究
巴金《激流三部曲》高觉新的悲剧命运
上市公司股权结构对经营绩效的影响研究
中国传统元素在游戏角色...
浅析中国古代宗法制度
现代简约美式风格在室内家装中的运用
高警觉工作人群的元情绪...