毕业设计说明书（论文）中文摘要掺杂态的聚苯胺是一种典型的导电高分子，其优异的电导率、可逆掺杂/去掺杂行为和良好的环境稳定性使得其引起广泛的研究，其聚合的机理也成为了研究的主要目标。本文研究了在中性与酸性水溶液条件下，合成邻甲氧基苯胺寡聚物，并进行核磁共振表征。采用过硫酸铵（以下简称APS）作为邻甲氧基苯胺聚合反应的引发剂，亚硫酸氢钠作为反应猝灭剂，反应体系恒温25℃在反应两分钟后猝灭。酸性条件采用0.01M的盐酸溶液达到。采用薄层层析与柱层层析分离寡聚物。探索了薄层层析的最佳展开剂配比。寡聚物采用一维和二维核磁共振进行表征，并用红外（FTIR）详细分析基团特征峰，用以推测苯胺聚合反应机理。63941

毕业论文关键词  聚苯胺    寡聚物  核磁共振  

毕业设计说明书（论文）外文摘要

Title    Synthesis, Separation and Characterization of  Anisidine oligomer in aqueous and colloidal system                                                 

Abstract Anisidine oligomer has been prepared from the neutral and acidic aqueous solution (in 0.01 M HCl).The polymerization, as initiated by APS, was quenched by sodium bisulfite after a reaction time of 2 minutes. Both thin layer chromatography and column chromatography were used to separate the oligomers. Both 1D and 2D NMR spectroscopies are employed to characterize the structures of these species,meanwhile FTIR is used to characterize the functional group of Anisidine ; accordingly a reaction mechanism for their formation is put forward. 

Keywords  Polyaniline    oligomer    NMR 

1 绪论 1

1.1聚苯胺的结构与命名 2

1.2聚苯胺的改性 2

1.2.1 掺杂改性 3

1.2.2接枝改性 3

1.2.3复合改性 3

1.2.4 其他改性 4

1.3聚苯胺的聚合机理 5

1.4聚苯胺导电机理 6

1.5 聚苯胺的应用 8

1.6 本课题研究的主要内容 9

2 邻甲氧基苯胺寡聚物的合成、分离与表征 1

2.1实验准备 1

2.2实验合成 2

2.3邻甲氧基苯胺寡聚物的分离、提纯 2

2.3.1邻甲氧基苯胺寡聚物的萃取 2

2.3.2邻甲氧基苯胺寡聚物的浓缩 2

2.3.3邻甲氧基苯胺寡聚物的分离 3

2.4产物分析及表征 4

2.4.1 酸性条件下邻甲氧基苯胺寡聚物核磁分析 6

2.4.2中性条件下邻甲氧基苯胺寡聚物核磁分析 10

2.5结果分析与讨论 12

致  谢 1

参考文献 2

1 绪论

众所周知，材料是人类社会发展的物质基础，是社会文明进步的象征。因此以材料的发展水平为标志，可将人类历史划分为石器时代、青铜器时代和铁器时代等。新材料的诞生，均不同程度地促进了整个社会的进步。如今导电高分子的出现，极大地丰富和方便了人民群众的生产与生活。