摘要为了提高阴离子交换膜的保水性及在高温低湿条件下的电导率，应用球磨法将亲水性阴离子交换树脂均匀分散于氯甲基化聚醚砜的溶液中，通过改变掺杂比制备了一系列不同含量的杂化膜。再经季铵化、碱化处理，将杂化膜转变为季铵碱形式的阴离子杂化膜。对所得杂化膜的电导率、吸水率、尺寸变化等进行了表征，发现在同样90℃的条件下，树脂含量为 5% 的阴离子交换膜的电导率可达34。04mS/cm，吸水率可达55%。结果表明，树脂含量为 5% 的阴离子交换膜具有最佳的综合性能。78503

毕业论文关键词  阴离子交换树脂，季铵化聚芳醚砜，离子电导率。

毕业设计说明书外文摘要

Title  Study on the Application of alkaline electrolyte membranes Modified by  Hybridation 

Abstract In order to improve the water retention of anion exchange membrane and the conductivity under the condition of high temperature and low humidity , ball grinding method was applied to the hydrophilic anion exchange resin dispersed homogeneously in the quaternary ammonium poly(arylene ether sulfone) solution。  By changing the doping than a series of different content of hybrid membrane was prepared。  Then through Friedel-Crafts chloromethylation, quaternization and alkalization , the hybrid membrane is changed into a quaternary ammonium alkali anion membrane。 Electrical conductivity of the obtained hybrid membrane, the water absorption and dimensional change of characterization, found 90 ℃ under the same conditions, the resin content is 5% of the anion exchange membrane conductivity can reach 34。04 mS/cm, bibulous rate is 55%。 The results show that the resin content is 5% of the anion exchange membrane has the best comprehensive performance。

Keywords  anion exchange resin, quaternary ammonium poly(arylene ether sulfone), ion conductivity。

目录

1 绪论 1

1。1  燃料电池 1

1。2  质子交换膜燃料电池 1

1。3  阴离子交换膜燃料电池 2

1。4  阴离子交换膜 2

1。5  离子交换树脂 4

1。6  本文研究意义及主要内容 5

2  实验部分 5

2。1  实验仪器及设备 5

2。2  原料与试剂 6

2。3  药品的精制与提纯 7

2。5  聚合物的氯甲基化 8

2。6  膜的制备和处理 8

2。7  性能表征 9

3  结果与讨论 12

    3。1  无规型阴离子交换膜的制备 12

3。2  尺寸变化 14

3。3  吸水率 15

3。4  电导率 16

3。5  机械强度 17

3。6  稳定性 17

3。7  溶解性 18

结论 20

致谢 21

参考文献 22

1 绪论

工业大文明的发展伴随着化石燃料资源的急剧枯竭，社会大文明的发展使得人们的环保意识的逐渐提高，因此寻找新的清洁替代能源逐渐成为越来越迫切的研究方向。燃料电池的出现无异于是旱林中的甘露，从发展到今天已经取得了显而易见的进展。