摘  要：由于掺氮石墨烯具有良好的稳定性和催化性能，而纳米氧化亚铜同样具有优异的电活性，所以近年来对掺氮石墨烯-氧化亚铜复合材料的研究也比较活跃。本论文以的氧化石墨和硫酸铜为原料，采用溶剂热法将单原子掺杂进入石墨烯晶格中，形成掺氮石墨烯，然后再将铜离子吸附在其表面，化学还原制备掺氮石墨烯-氧化亚铜复合材料，通过SEM、XRD表征技术对掺氮石墨烯-氧化亚铜复合材料进行一系列的表征和分析，确定该复合材料的组成和结构。以此材料构建电化学传感器，并用于检测生物小分子多巴胺，研究其电催化性能。79629

毕业论文关 键 词：掺氮石墨烯，掺氮石墨烯-Cu2O复合材料，多巴胺，电催化

Abstract: Due to its excellent stability and catalytic activity of nitrogen doped graphene, and good electroactivity of Cu2O, in recent years the study of nitrogen doped graphene-Cu2O composite has been attracting more and more attention。 In this paper using graphite oxide and urea as raw material, nitrogen doped graphene was first prepared by solvothermal method。 Then copper ions will be loaded on the surface of nitrogen doped graphene, and reduced by ascorbic acid(AA) at room temperature。 As a result, nitrogen doped graphene-Cu2O composite was finally obtained after washing and drying。 The products were characterized by SEM and XRD to confirm their composition and mircostructure。 Electrochemical sensors were constructed to determine dopamine so that the electrocatalytic performance will be revealed clearly。 

Keywords: nitrogen-doped graphene, nitrogen-doped graphene-Cu2O composite, dopamine, electrocatalysis

目  录

1  前言 3

1。1  石墨烯的基本性质研究 3

1。1。1  石墨烯的结构和性质 3

1。1。2  石墨烯的制备 3

1。1。3  石墨烯的应用 4

1。2  掺氮石墨烯的概述 5

1。3  氧化亚铜的概述 5

1。3。1  氧化亚铜的结构和性质 5

1。3。2  氧化亚铜的制备 6

1。3。3  氧化亚铜的应用 6

2  掺氮石墨烯—氧化亚铜复合材料的制备 7

2。1  实验部分 7

2。1。1  实验试剂 7

2。1。2  实验装置 7

2。1。3  样品的制备及表征 8

3  掺氮石墨烯—氧化亚铜复合材料的电催化性能测试 10

3。1  电化学传感器 10

3。2  实验准备 10

3。2。1  产品处理 11

3。2。2   玻碳电极的打磨与清洗 11

3。2。3  缓冲溶液的配制与处理 11

3。3  电催化性能的测试 11

结  论 13

参 考 文 献 14

致  谢 15

1  前言

1。1  石墨烯的基本性质研究

1。1。1  石墨烯的结构和性质