摘要环氧树脂具有化学稳定性好、粘接性和电绝缘性高等特点，通过何种方法制备水性环氧树脂成为各国研究水性涂料的重点。本论文进行了水性环氧树脂及其涂料的制备研究。利用转相乳化法制备了水性环氧树脂，探讨了乳化温度、乳化剂种类和用量、HLB值、加水量等因素对制备的水性环氧树脂乳液稳定性的影响。使用最佳乳化条件制备了较稳定的水性环氧树脂乳液。将制备的水性环氧树脂乳液运用到涂料中，通过对涂料的性能测试，探讨了不同固化剂种类及用量对涂料性能的影响，进而得到固化剂的最佳用量。10331
- 上一篇：完全充填细小空隙下丙烯酰胺水凝胶的制备
- 下一篇：低温变色材料的制备及其变色性能的研究
关键词 转相乳化 水性环氧树脂 固化剂 涂料
毕业设计说明书（论文）外文摘要
Title Study on the preparation of waterborne epoxy resin coating
Abstract
Epoxy resin has good chemical stability and high performance of adhesion, electricity insulating. It is a keystone of every nation how to manufacture the waterborne epoxy resin in waterborne coating’s industry. The preparation of waterborne epoxy resin coating was studied in the paper. Waterborne dispersions of epoxy resin were prepared by the so-called phase-inversion emulsification technique. The influence factors on stable waterborne epoxy resin such as emulsification temperature, HLB, emulsifiers and water content were investigated. High stable epoxy emulsion can be prepared from the choice of optimum emusifiers and technological reactive conditions. The stable epoxy emulsion was used to prepare waterborne epoxy resin coatings afterwards. The influence of curing agent content on coating performance was discussed by testing of the coating, then the optimum content was obtained.
Keywords phase-inversion emulsification waterborne epoxy resin curing agent coating
目 录
1 绪论 1
1.1 环氧树脂 1
1.2 环氧树脂水性化的方法 4
1.3 微乳化技术基本原理 8
1.4 乳液性能表征 12
1.5 水性环氧固化剂 13
1.6 水性环氧树脂涂料的应用 16
1.7 本课题研究意义 18
2 实验部分 19
2.1 实验仪器 19
2.2 实验试剂 19
2.3 水性环氧树脂的制备 19
2.4 水性环氧树脂乳液稳定性的测试 20
2.5 水性环氧树脂涂料的制备 20
2.6 水性环氧树脂涂料的表征 23
3 结果与讨论 24
3.1 乳化工艺条件对环氧树脂乳液稳定性的影响 24
3.2 水性环氧树脂涂料的配方设计 26
3.3 水性环氧树脂涂料的性能测试 28
3.4 小结 29
结论 30
致谢 31
参考文献 32
1 绪论
涂料有着悠久的历史，从利用动物的油脂和树上分泌的树脂等为成膜物，发展成为主要以石化产品合成的高分子聚合物为成膜物，人们进行了长期的探索。涂料的生产和使用也是从一种世代相传的技艺发展成为涉及多学科的现代化的涂料工业。随着社会的发展，人们对涂料性能的要求也越来越高，各国也相继出台法规限制VOC（挥发性有机化合物）的排放量。而传统的涂料中含有大量的VOC，因此发展环境友好型的涂料成为涂料领域的研究热点，于是水性环氧树脂涂料就在这种背景下应运而生。