摘  要：现代无损检测与评价技术不但要探测缺陷的是否存在，还要给出有关缺陷的定量检测结果。为了达到定量无损检测的最终目的，完成检测定量化的最终形式，本文利用ANSYS高级分析技术APDL，分析了不同热激励形式作用下表面温度与时间的关系，得出了不同缺陷形态的被测对象在幅值和频率调制激励下的实验仿真结果，进而分析了外表温度变化与调制幅值和频率之间的关系，为基于相位分析热层析重建打下了基础。79075

毕业论文关键词：无损检测，红外热波检测，参数化，ANSYS，APDL

Abstract: The technology of modern nondestructive test (NDT) and evaluation is not only aim to detect the defects’ being or not, but also to reach a quantitative detection result 。 In order to achieve the final goal of quantitative NDT and the final form of the testing quantification, this thesis applies the ANSYS advanced analysis technology APDL。 It analyzes the relation between surface temperature and time under the effect of different thermal prompting; then concludes the simulation result of the detected object with different kinds of defects under the drive of the amplitude and the frequency modulation; therefore analyzes the relationship between surface temperature change with the amplitude and frequency modulation; and finally lays the foundation for the rebuild of thermal chromatography on the basis of phase analysis。

Key words: Nondestructive Test (NTD), Infrared thermal wave detection, Parameterization, ANSYS, APDL

目   录

1  绪论 5

1。1  课题研究的目的及意义 5

1。2  热波成像的意义 5

1。3  课题设计及要求 5

2  热波成像检测 6

2。1  热波成像的原理 6

2。2  热波成像检测技术的原理 6

2。3  热波成像检测方法 7

2。4  热波成像检测技术特点 8

2。5  热波成像检测技术的应用 9

3  有限元分析基本理论 10

3。1  有限元分析和ANSYS高级分析技术APDL 10

3。2  有限元热分析基本原理 11

3。3  稳态热分析和瞬态热分析 11

3。4  热波成像检测的有限元分析 12

4。  实验仿真 13

4。1  几何建模 13

4。2  施加载荷计算 16

4。3  仿真结果 16

4。4  调制激励下的仿真 17

结论 23

参考文献 24

1  绪论

1。1  课题研究的目的及意义

    由于复合材料的应用越来越广泛，越来越无法替代，所以，复合材料的检测就变得很重要了。热波检测技术就是在这样的情况下得到了快速的发展，并越来越受到重视。

    热波成像检测虽然优点突出，但是也极易受到干扰，所以其定量检测水平较低。多数热波成像检测只是定性检测，通常还需要配合其他检测方法做进一步的测量，如此检验下来的结果就很难让人满意了。