摘要为了探明剧烈变形后时效强化铝合金的抗局部腐蚀的潜力，本论文选择2519A 为研究对象，借助于金相显微镜、扫描电镜等手段，采用 Tafel 实验、浸泡实验法研究了单道次 ECAP 变形再时效后该合金的晶间腐蚀、剥落腐蚀性能。结果表明：经 ECAP 塑性变形的 2519A 铝合金的抗晶间腐蚀性能较固溶态合金高，但抗剥落腐蚀性能低于固溶态合金；变形合金进行 180℃时效处理，随着时效时间的延长，晶间腐蚀深度呈先升后降的趋势，从 85.2μm 上升到 288.0μm 再逐渐下降到 213μm；合金的剥落腐蚀等级虽然变化很小，其严重程度却基本呈先降后升趋势。时效温度的提高，对合金晶间腐蚀影响较小，剥落腐蚀严重程度显著加强。  21603
毕业论文关键词   2519A 铝合金  ECAP 塑性变形  局部腐蚀  时效
Title    Study on localized  corrosion of severe plastic deformed 2519A aluminum alloy 
 Abstract
To explore the localized corrosion potential of age-hardening aluminum
alloy subjected to severe plastic deformation, we choose aluminum alloy
2519A as object. By optical microscope and scanning electron microscope 
the properties of localized corrosion on  2519A aluminum  alloy after  plastic
deformation  by  ECAP  after  one-pass  and  aging  were studied by immersion test
and Tafel test. The results show that intergranular corrosion depths for
samples after one pass ECAPed were sharply decreased compared to samples
after solid solution  treatment，but exfoliation corrosion resistance shows
the opposite tendency.  As time gose on,  the intergranular corrosion
propagation depths was found  raised  at first, then decreased,  form
85.2μ m  to 288.0μ m  than  decrease  to 213.5μ m,  but  diametrically opposite
condition was found in the exfoliation corrosion in the 2519A aluminum
alloy aged at 180℃. As the aging temperature increases, the influence of
intergranular corrosion  was decreased, but  the exfoliation corrosion just the opposite.
Keywords    2519A aluminum  ally  ECAP  localized corrosion  aging
目    录  ..I
1   引言  .1
1.1   等通道转角挤压技术概述 .1
1.2   铝合金腐蚀  .3
1.2.1  铝合金晶间腐蚀 4
1.2.1.1  铝合金晶间腐蚀理论 ..4
1.2.1.2  铝合金晶间腐蚀影响因素 5
1.2.2  铝合金剥落腐蚀 6
1.2.2.1  铝合金剥落腐蚀理论 ..6
1.2.2.2  铝合金剥落腐蚀影响因素 6
1.3  本课题研究的意义  8
2   实验  .8
2.1   实验材料  ..8
2.2   实验仪器  ..8
2.3   样品制备及实验方法 9
2.3.1  实验流程  9
2.3.2  样品制备  9
2.3.3  实验方法   10
2.3.3.1 TAFEL 极化曲线测试  .. 10
2.2.3.2  晶间腐蚀 . 10
2.3.3.1  剥落腐蚀 . 10
3   实验结果  .. 10
3.1  Tafel极化曲线   11
3.2   晶间腐蚀  .. 11
3.3   剥落腐蚀  .. 13 4     . 18
4.1 ECAP大塑性变形对铝合金腐蚀性能的影响  .. 18
4.2.  热处理制度对铝合金腐蚀性能的影响  19
结   论   22
致   谢   23
参  考  文  献  .. 24
 
 1   引言
随着科学技术的飞速发展，航空航天技术、军事工业和交通运输领域对制造材料 大变形2519A铝合金局部腐蚀行为研究:http://www.youerw.com/wuli/lunwen_13871.html