摘要本文利用LY12铝合金作为试验材料，针对螺柱熔化焊易出现偏焊、未熔合、裂纹等问题，充分利用固相焊接头性能好的优点，提出摩擦螺柱焊接工艺试验研究，通过针对不同直径之间的棒材与螺柱的焊接，研究转速、摩擦压力、顶锻压力、顶锻时间等焊接参数对焊接接头性能的影响。并通过金相组织分析、电镜扫描以及拉伸试验等对焊接接头进行分析，得出最佳焊接工艺参数。通过对参数的不断匹配，将螺柱焊往机械化和自动化方向进行研究，最终为机器人螺柱焊接装置和系统设计提供依据。67499

毕业论文关键词：LY12铝合金  摩擦焊螺柱焊  组织 力学性能

毕业设计说明书（论文）外文摘要

Title  High strength alloy friction stud welding technology research 

Abstract

In this paper , LY12 aluminum alloy as test material for fusion weiding stud weiding to bias , lack of fusion , cracks and other problems , make full use of solid-phase welding head performance advantages, friction stud welding process proposed experim ental study, by targeting different diameters between the bars and sud welding , research speed , friction pressere , the top forging force , upsetting time welding parameters on weld joint performance .And thtough microstructure analysis , scanning electron microscopy and tensile testing of welded joints and other analysis , the optimum welding parameters . Through the constant parameters match , stud welding directiong towards mechanization and automation research and , ultimately , the robot stud welding device and system design to provide the basis .

Keywords ：LY12 aluminum alloy    Friction Stud welding    Organization  Mechanical properties

目次

1  引言 1

1.1  选题意义及背景 1

1.2高强铝合金的研究现状及进展 2

1.3  摩擦焊 3

1.4  螺柱焊接 8

1.5  本课题主要研究内容 13

2  实验条件、焊接设备、检测设备 13

2.1  实验材料 13

2.2  焊接设备 15

2.3  检测设备 16

3  高强铝合金摩擦螺柱焊接设计 17

3.1  高强铝合金摩擦螺柱焊整体设计思路及难点 17

3.2  LY12摩擦螺柱焊试验方案 18

3.3  本章小结 19

4  LY12摩擦螺柱焊实验过程及结果分析 20

4.1  实验操作步骤 20

4.2  实验过程中的参数控制 21

4.3  本章小结 25

5  组织及力学性能分析 26

5.1  高强铝合金摩擦螺柱焊接接头组织分析 26

5.2  电镜扫描分析 27

5.3  拉伸试验 28

5.4  本章小结 28

6  结  论 29

展望 30

致  谢 31

参 考 文 献 LY12高强铝合金摩擦螺柱焊接工艺试验研究:http://www.youerw.com/cailiao/lunwen_75724.html