摘 要不锈钢复合管因为同时具有两种钢的特性，并且价格低，适用性广的特点而被广泛应用于石油输送、西气东输、以及许多其他的民用工程。本文将先对以往的普通焊接方法下的复合管试样进行分析，发现了热影响区焊缝的硬度梯度，分析了其中的原因是热输入过大，决定采取热输入量小的工艺如：采用手工电弧焊、GES316L不锈钢焊丝打底，E4303碳钢焊条进行填充盖面焊。完成了对复合钢管316L/20钢的对接。并且在光学金相显微镜、维氏显微硬度计等仪器的帮助下对焊缝接头进行了微观组织成分分析和力学性能分析。87014

结果发现了复合管焊接时，在进行填充层已经盖面层的焊接时使用小电流以降低焊接热输入，有助于改善热影响区硬度梯度的问题。为以后复合管手工电弧焊的方面提供了科学的参考依据。

毕业论文关键词：不锈钢复合管；手工电弧焊；降低热输入；力学性能

Abstract Stainless steel composite pipe because both properties of both steels, and the price is low, wide applicability of the characteristics have been widely used in petroleum transportation, natural gas, as well as many other civil engineering。 This article will first composite pipe specimens under conventional general welding method were analyzed and found that the heat affected zone of the weld hardness gradient, analyzed the reason is the heat input is too large, decided to take a small amount of heat input processes such as: using SMAW, GES316L stainless steel wire base, E4303 carbon steel electrode filled capping。 Finished composite steel 316L / 20 steel butt。 And with the help of an optical microscope, micro Vickers hardness tester and other equipment under the weld joints microstructure composition analysis and mechanical analysis。

The results found that the composite pipe welding, reduce heat input can effectively reduce the weld fusion zone hardness of ups。 For subsequent welding composite pipe provides a scientific basis。

Keywords：Composite pipe；SMAW；Reduce heat input；Mechanical analysis。

目 录

第一章 绪 论 1

1。1 立项背景与研究意义 1

1。2焊接材料的发展 2

1。3不锈钢复合管制备方法 3

1。3。1机械结合复合管制备方法 3

1。3。2冶金结合复合管制备方法 4

1。4复合钢管研究现状及存在问题 5

1。5双相不锈钢简介 8

1。6本课题研究内容 10

第二章 复合管焊接成品力学性能检测 11

2。1引言 11

2。2复合钢管规格参数 11

2。3复合管焊接接头金相分析 12

2。3。1实验目的 12

2。3。2实验器材 12

2。3。3试样的制备与金相分析 13

2。2。4观察金相以及拍摄金相照片 14

2。4复合管焊接接头硬度分析 16

2。4。1实验目的 16

2。4。2实验器材 16

2。4。3显微硬度的测定 17

2。4。4显微硬度数据分析