摘要生物组织激光焊接技术是一种微创手术技术，具有时间短、愈合快、瘢痕不明显、操作简单等优点。但是目前存在的问题是缺乏系统分析激光参数和其他相关因素对焊接组织吻合效果的影响，由于影响因素多，导致该技术可重复性较低，组织粘合的潜在机理尚不明确。本文采用实验研究手段，以离体猪皮为试验样本，主要探索激光参数如功率、扫描方式、波长等和助焊剂等因素对式样焊接效果的影响。87869

实验结果表明，连续激光器相比，高功率脉冲激光焊接的时间大大减少，提高了效率，BSA可以加速切口粘连；5W激光脉冲，脉冲持续时间为50ms，光斑半径为0。2mm，焊200mm的线扫描速度），BSA处理切口，焊接成功率是非常高的，具有可重复性。

毕业论文关键词  激光焊接  生物组织  激光功率  BSA     

毕业设计说明书外文摘要

Title    Study of Laser Biological Tissue Welding(LTW)                     

Abstract The laser welding technology of biological tissue is a minimally invasive technique, which has the advantages of short time, quick healing, no obvious scar, simple operation and so on。 But the existing problem is lack of systematic analysis of laser parameters and other factors influence on weld structure results, due to many factors, leading to the technology to be low repeatability and potential mechanism of tissue adhesion is not clear。 In this paper, the experimental research method, mainly to explore the effect of laser parameters factors such as power, scanning, wavelength and flux on the pattern welding effect。

Experimental results show that compared with continuous laser, high power pulse laser welding time is reduced significantly, improve efficiency, BSA can be accelerated incision adhesion; 5W pulse laser, pulse duration of 50ms, spot radius 0。2mm, welding speed of 200mm / s line scan), incision of BSA treatment, welding success rate is very high, with repeatability。

Keywords   Laser welding  biological tissue  Laser power  BSA

目次

1  绪论 1From+优·尔*论^文W网wWw.YouErw.com 加QQ752018.766

1。1  生物组织激光焊接 1

1。2  生物组织激光焊接研究概况 1

1。3  本试验的主要研究内容 4

2  离体生物组织激光焊接试验系统 5

2。1  确定激光波长 5

2。2  生物组织激光焊接试验平台 5

3  离体生物组织激光焊接工艺试验。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。9

3。1 试验 9

3。2 实验步骤。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。10

4  离体生物组织激光焊接工艺试验结果分析。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。12

4。1 激光功率对试验结果的影响。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。。12