摘要本课题研究了8mm厚的5754铝合金螺旋管的TIG自动焊接工艺，分析了接头组织及性能。结果表明，TIG自动化焊接可以形成外观良好的焊缝，适合的焊接参数为：内焊机电流为270~275A，外焊机电流为300~305A，内焊机电压为17.5~17.7V，外焊机电压为20~20.5V，焊速0.20m/min，外焊送丝速度1.90m/min，内焊送丝速度1.80m/min，接头的微观组织均匀，无明显缺陷。焊接接头显微硬度试验得到：显微硬度为母材的96%。焊缝质量好，达到要求。并进行了铝合金试板双面双弧平焊工艺探索，为进一步完善螺旋管的自动化焊接生产工艺奠定试验基础。68174

毕业论文关键词  5754铝合金螺旋管  TIG自动焊接  微观组织  显微硬度试验  

毕业设计说明书（论文）外文摘要

Title  Continuous production investigation of TIG automatic welding process for Spiral Pipe with Aluminium alloy       

Abstract

This subject aimed to experimentally explore the microstructure and properties of joints undergoing TIG automatic welding with 8mm thick Spiral Pipe with Aluminium alloy. The results show that TIG automatic welding could fit the requirement of spiral Pipe welding. The process parameter for TIG automatic welding was obtained and the sound welds can be obtained under the condition of a welding speed of 0.20m/min, a inside welding current of 275~270A, a outside welding current of 305~300A，a inside welding voltage of 17.7~17.5V, a outside welding voltage of 20.5~20V，Outer welder wire feed speed of 1.90m/min. Internal welding wire feed speed of 1.80m/min.The joints had a fine microstructure and no conspicuous welding defects. Also,the microhardness of joints is 96% of base metal.In addition, the test assistant research 8mm double-sided double-arc TIG welding for Spiral Pipe with Aluminium alloy。

Keywords  Spiral Pipe with Aluminium alloy    TIG automatic welding microstructure    microhardness testing

目录

1  绪论 1

1.1  课题背景及选题意义 1

1.2  铝合金焊接性分析 1

1.2.1  铝镁合金焊接特性 1

1.2.2  铝镁合金焊接缺陷 2

1.2.3  铝合金缺陷的防止措施 3

1.3  TIG焊接研究现状 4

1.4  螺旋管生产工艺研究现状 6

1.4.1  螺旋焊管应用现状与发展 6

1.4.2  螺旋管的生产过程 6

1.5  本课题主要研究内容 8

2  螺旋管TIG自动化焊接方法设计 10

2.1  铝镁合金螺旋管焊接难点分析 10

2.2  螺旋管TIG自动化焊接系统构建 10

2.3  母材、焊材和工艺设备 11

2.3.1  试验材料 11

2.3.2  试验设备 12

2.4  微观组织力学性能试验 14

2.4.1 显微硬度试验 14

2.4.2 拉伸试验 15

3  铝合金螺旋管双面TIG自动化焊接工艺试验研究 16

3.1  铝合金螺旋管生产过程