摘要：环氧树脂混凝土是用环氧树脂代替或部分代替水泥,掺入适量固化剂、增塑剂、稀释剂及填料作为胶粘剂,以砂、石作为骨料,经混合、成型、固化而成的一种新型复合材料，在机床生产，桥梁加固，建筑补强等领域有广阔前景。本实验主要研究混凝土抗压强度与含胶量，固化剂和空隙率之间的关系。结果表明：含胶量越大，固化剂含量越多，空隙率越低，抗压强度越高。61098

毕业论文关键词：环氧树脂   环氧树脂混凝土   抗压强度     

Title  The research on the strength of the epoxy resin concrete

Abstract Epoxy resin concrete is a new type of composite material, using epoxy resin to replace or partly replace cement, mixed with suitable amount of curing agent and plasticizer, diluent and packing as adhesive, sand and stone as aggregate, after mixing, molding and curing. It has broad prospects in machine tool production, bridge reinforcement and construction reinforcement. This experiment mainly study the relationship between the concrete compressive strength and the amount of resin content, curing agent and the porosity.The results indicate that the more resin content,the more curing agent,the lower porosity,the higher compressive strength.

Keywords   Epoxy    Epoxy resin     compressive strength

毕业设计说明书（论文）外文摘要

 1  绪论 1

1．1  环氧树脂 1

1．2  环氧树脂混凝土 2

1.2.1  环氧树脂混凝土的配料组成 2

1.2.2  环氧树脂混凝土的制备 3

1.2.3  环氧树脂混凝土的性能 5

1.2.4  环氧树脂混凝土在实际中的应用 7

2  实验 8

2．1  实验原料 8

2.1.1  环氧树脂和固化剂的选择 8

2.1.2  稀释剂与脱模剂的选择 10

2.1.3  骨料（碎石）级配 10

2．2  实验仪器 11

2．3  实验步骤 12

2.3.1  试样制备： 12

2.3.2  试样测试： 13

3  实验结果与分析 14

3．1  含胶量对抗压强度的影响 14

3．2  固化剂含量对抗压强度的影响 16

3．3  空隙率对抗压强度的影响 18

结  论 23

致  谢 24

参考文献 25

 1  绪论

传统的机床结构材料主要由钢和铸铁组成，具有良好的切削性能、较高的刚度和强度等特点。它们可以铸成复杂的形状, 易加工, 加工精度也高, 加工质量好, 但其生产周期长、废品率高、阻尼特性不突出等缺点也很明显。其中高速切削机床床身单元是机床的核心部件，而高速切削机床床身系统的动态特性的优劣，又直接影响着加工质量。高速切削机床床身的材料必须满足高精度、高刚性、高寿命、高阻尼和高热稳定性的要求[1] 。

近年来, 国内外积极开展用新型材料替代传统金属材料制造机床床身的研究开发工作, 研究采用聚合物混凝土作为精密机床的支承件[2-5], 并取得了一定的成就。