摘要针对Mg-PTFE红外辐射材料燃速控制技术，在理论研究的基础上，重点研究能够降低燃速并且能基本保持红外辐射性能不变的添加剂。探讨了薄片型红外辐射材料及制备工艺对红外辐射性能的影响，选择不同的添加剂加入到配方当中，研究添加剂及不同含量对Mg-PTFE薄片型红外辐射材料的辐射性能和燃速的影响。分析确定了它们在红外辐射材料当中的最佳含量，得出诱饵剂的红外辐射亮度随配方中TJ的增加而有所升高，随着乌洛托品的减少而降低的结论。68585

毕业论文关键词   红外诱饵剂  辐射强度  燃速   

毕业设计说明书（论文）外文摘要

Title     The research on the burning rate control technology    of infrared radiation materials based on  the    Mg-PTFE                                              

Abstract

On the basis of theoretical research ， I focus on the additives that can reduce the burning rate and keep the infrared radiation properties basically unchanged for the burning speed control technology of Mg-PTFE infrared radiation materials . As well as , I investigate the infrared radiation materials with sheet shape and the preparation crafts’influence on the performance of infrared radiation . After a choice ， the various additives are added to the recipe . After that , I research the additives and their different content’s influence on Mg-PTFE infrared radiation materials’radiation properties and burning rate . And then , I analysis to determine their optimum content in the Infrared radiation properties.

Keywords  Point source infrared decoy agent ；   Radiation intensity；

          Burning rate

目   次

1 绪论 1

1.1 课题研究背景和意义 1

1.2 红外诱饵剂国内外研究现状 1

1.3 本论文主要研究工作 1

2 红外辐射理论与燃速控制方法研究 5

2.1 红外辐射基本原理 6

2.2 Mg-PTFE薄片燃速控制方法研究 7

3 Mg-PTFE燃速控制实验 9

3.1 Mg-PTFE薄片制备工艺 9

3.2 实验主要仪器与材料 10

3.3 不同添加剂对燃速的影响 11

3.4 选择出合适的燃速控制添加剂 12

4 添加剂对Mg-PTFE薄片燃速和红外辐射特性的影响 13

4.1 实验样品 13

4.2 测试仪器 13

4.3 结果与分析 17

结论 27

致谢 28

参考文献 29

1 绪论

1. 1 课题研究背景和意义

由于现代光电子技术的快速发展推动了红外制导技术的发展和完善，不同种类的精确制导武器相继涌现，尤其是红外制导导弹慢慢显示出其特有的优势和其巨大的作战威力。使得制导武器对预定目标的命中率和打击力度有大幅提高，所以在现代化战争中，作战飞机、船舰、装甲车以及其他地面工事等就会受到精确制导武器的严重威胁，红外制导导弹已经成为作战飞机和船舰等作战设施设备最具威胁性的“敌人”[1]。