摘要对包覆材料改性是近几年国内外研究的热门课题。该实验的基础物质为包覆料原料，由乙基纤维素和增塑剂组成，有较好的相容性。改性料为聚己内酯（PCL），熔点低，柔韧性好，有优良的热塑性。本文旨在通过改变包覆料原料与聚己内酯之间的配比制备新的混合物，用系统的实验方法，找到其屈服强度、弹性模量、断裂强度、延伸率、抗拉强度与配比之间的规律，验证是否能增强包覆料原料的综合力学性能，同时介绍了对混合工艺的探索和表征方法。74282

毕业论文关键词  包覆材料 改性 配比 规律 混合工艺 表征方法

毕业设计说明书外文摘要

Title  Research and modification of thermoplastic coating materials used for propellants

Abstract It is the hot topic in the research both at home and abroad in recent years on the coating material modified。 Coating material, the basis of the material, which is composed of ethyl cellulose and plasticizer, has good compatibility。 Polycaprolactone (PCL) is used as Modified material,owns low melting point, good flexibility, excellent thermoplastic。 The aim of this paper is to change the features of coating material with PCL by adjusting the ratio between them to produce new  mixtures。 It is hopeful to find the rules between the ratio and the yield strength, elastic modulus, tensile strength, elongation, verifying whether PCL can reinforce coating material mechanical properties。 Mixed process and characterization methods are introduced at the same time。

Keywords: modified，coating material，mixed process, characterization method

目   次

1  引言 1

1。1  研究包覆材料改性的必要性 1

1。2  包覆材料研究现状 1

1。3  研究目的 2

2  实验部分 4

2。1  实验材料 4

2。2  实验仪器及设备 4

2。3  样品制备方法 5

2。4  切片方法介绍 7

2。5  拉伸性能测试 8

2。6  3D打印实验 9

2。7  表征方法 9

3  结果与分析 12

3。1  直观现象 12

3。2  拉伸性能数据分析 12

3。3  原因分析 14

3。4  密度测试结果 16

结论 17

致谢 19

参考文献 20

1  引言

1．1  研究改性包覆材料的必要性

包覆材料是固体火箭发动机火箭装药的重要组成部分，包覆材料的直接作用对象是推进剂。推进剂指的是有规律地燃烧释放出能量，产生气体，推送火箭和导弹的火药。用于火箭发射能量供给的药剂的发展历程依次为黑火药、双基推进剂、复合推进剂、改性双基推进剂。就理论比冲而言，改性双基推进剂和和复合推进剂的比冲更大，即能量水平更高，但是改性推进剂的爆轰敏感度和机械敏感度大[1]。随着研究人员的不断深入以及社会科技的进步，推进剂的输出能量密度越来越高，若没有包覆材料这一中间介质，则不能使燃烧限制在特定的表面上，获得特定的压力—时间曲线；同时包覆层具有隔热作用，可避免推进剂产生的燃气直接接触发动机内壁，对发动机的使用状态起到保护；更重要的是，推进剂在制造、搬运、存仓过程中无可避免地要受到摩擦、撞击的影响，包覆层则可起到缓冲作用。论文网