摘要：论文成功地将蛋氨酸（Met）修饰硅基到介孔材料SAB-15上，合成了His-SBA-15，通过XRD, FT-IR, XPS, N2吸附-脱附实验手段对材料的进行了表征，实验结果表明，蛋氨酸成功地嫁接在材料表面，且材料的结构基本保持不变。论文研究了His-SBA-15对重金属离子Hg2+的吸附性能。论文考察了溶液pH值、吸附时间和吸附剂用量对Ni2+吸附效果的影响，结果表明，蛋氨酸修饰硅基介孔材料对Ni2+具有较好的吸附效果。75914

毕业论文关键词：硅基介孔材料，蛋氨酸，Hg(II)，吸附

Abstract：Mesoporous silica material SBA-15 functionalized with methionine was synthesised in this paper successfully。 The structures, surface adsorption properties and pore sized distribution of the synthesized materials SBA-15，NH2-SBA-15 and Met-SBA-15 were characterized by XRD, FT-IR, XPS, N2 adsorption-desorption and thermo gravimetric analysis。 The results indicated that methionine was successfully anchored on the SBA-15 surfaces, the ordering of the inorganic support was preserved during the chemical modifications and the materials had better thermo stability。 The adsorption property of modified materials for Hg2+ was also studied。 The factors which may influence the efficiency of the adsorption, such as pH, contact time and the concentration of the solution was optimized。 The results indicated that Met-SBA-15 had good adsorption performance to Hg2+。

Key words: Silicon-based soporous materials; Methionine; Hg(II); Adsorption performance

目录

1前言 4

1。1有序介孔材料的发展 4

1。1。1 硅基介孔材料 4

1。1。2 硅基介孔材料的应用 4

1。2 SBA-15的研究进展 4

1。2。1 SBA-15的研究现状 4

1。2。2 SBA-15的改性研究 4

1。3 本论文的研究意义和内容 5

1。3。1研究意义 5

1。3。2研究内容 5

2。1 实验部分 6

2。1。1 药品与试剂 6

2。1。2 测试仪器 6

2。2 材料的合成 7

2。2。1 介孔分子筛SBA-15的制备 7

2。2。2 介孔分子筛SBA-15 的蛋氨酸改性 7

2。2。3 吸附实验 7

2。3 结果与讨论 8

2。3。1 样品的表征方法 8

2。3。2 表征分析 9

2。3。3 pH和时间的影响： 15

2。3。4 吸附动力学研究 16

结  论 19

参考文献 20

致谢： 25

1前言

1。1有序介孔材料的发展

1。1。1 硅基介孔材料

介孔材料是一种孔径介于微孔与大孔之间的具有巨大表面积和三维孔道结构的新型材料。按照化学组成分类，介孔材料一般可分为硅系和非硅系两大类。硅基介孔材料孔径分布狭窄，孔道结构规则，并且技术成熟，研究颇多。硅系材料可用催化，分离提纯，药物包埋缓释，气体传感等领域。硅基材料又可根据纯硅和掺杂其他元素而分为两类。进而可根据掺杂元素种类及不同的元素个数不同进行细化分类。杂原子的掺杂可以看作是杂原子取代了原来硅原子的位置，不同杂原子的引入会给材料带来很多新的性质，例如稳定性的变化、亲疏水性质的变化、以及催化活性的变化等等。