摘要：以对二(1,2,4-三氮唑基甲基)-苯（bis(1,2,4-triazole-yl-methyl)– benzene, BTX）为第一配体，以反式-1，4-环己二羧酸（1,4-cyclohexane dicarboxylic acid， 1,4-H2CHDC）和2,5-噻吩二羧酸（2,5-Thiorhene dicarboxylic Acid, 2,5-H2TDC）为第二配体，利用水热合成法制备得到了两个含锌的金属-有机骨架配合物（Metal-Organic Frameworks, MOFs）。单晶X-射线衍射表明化合物1 (C20H22N6O4Zn)和化合物2()分别都结晶于正交晶系，分别具有二维和三维骨架结构。83696

毕业论文关键词：配体；水热合成法；晶体结构

Based on the synthesis and crystal structure of the flexible mixing acid ligands of Mofs。

Abstract: of bis (1,2,4-triazole-yl-methyl) - benzene as the first ligand，Terephthalic acid and 2,5-thiophene-dicarboxylic acid as the second ligand, Prepared by hydrothermal synthesis to give a compound of the two compounds and two, respectively, one and two dimensional crystals, And they were a single crystal X-ray diffraction, The results show that Compounds 1 and two belong to the orthorhombic In this paper, the synthesis of the two compounds and the crystal structure was analyzed。

Keywords: ligand; hydrothermal synthesis; crystal structure

目    录

摘  要 1

引  言 2

1 实验部分 3

1。1 仪器与试剂 3

1。2 配体的制备 3

1。3 晶体的制备 3

2 结果与讨论 4

2。1 化合物的组成分析 4

2。2 X射线衍射及晶体结构 5

3 结  论 10

参考文献 10

致  谢……13

基于柔性羧酸混合配体的MOFs的合成与晶体结构

引言：金属有机骨架（Metal-Organic Frameworks, MOFs）材料是一种新型的多孔材料，具有比表面积和孔隙率较高，孔道尺寸和功能容易调节等特点，在气体存储、吸附分离和催化等多个领域有潜在应用。尽管人们按照晶体工程学的设计思想已设计合成了多种新颖结构的MOFs，但基于柔性混合羧酸类MOFs材料的合成以及性质的研究目前已成为前沿研究课题之一。

    本论文中选取了二种柔性的多元羧酸类的有机配体，依据配位化学和晶体学基本原理，利用水热法，合成了二个具有高维结构的MOFs材料，并采用X-射线单晶衍射对其进行了结构表征；并对柔性混合羧酸类MOFs材料合成方法以及它们的高维结构的形成规律进行了初步总结。金属或有机配体的原位反应的研究在配位化学和有机化学领域具有重要意义。人们可以通过金属或有机配体的原位反应发现许多新的有机反应，研究反应机理，还可以得到新型的、不能够通过常规的直接合成方法得到配位聚合物。这些原位反应现已成为构筑具有高空旷度的，具有光、电、磁学特性MOFs材料的重要方法之一。近些年来人们通过水热合成法合成了许多丰富多样的具有较好的物理化学性质的MOFs材料。来:自[优E尔L论W文W网www.youerw.com +QQ752018766-

   本文通过以对二(1,2,4-三氮唑基甲基)-苯配体，再分别以反式-1，4-环己二羧酸和2,5-噻吩二羧酸为第二配体，通过水热合成方法与Zn(NO3)2组装得到一维和二维层状化合物。作为MOFs材料或配位聚合物合成方法的一种补充，将这种水溶剂原位反应与晶体工程结合，可以得到一些通过常规合成方法无法得到的多功能晶体材料。