(4)CaF2 can decrease the viscosity of refining slag, improve the fluidity of slag and increase the mass transfer between steel and slag, which is beneficial to the desulfurization reaction。 On the other hand, CaF2 will erode the lining, the pursuit of the desulfurization effect blindly increasing the content of CaF2  is not desirable。

(5)LF refining slag desulfurization test found a slag type of better desulfurization effect, the content of its components for CaO-50%, SiO2-16%,A12O3-20%, MgO-10%,

CaF2-4%, two element alkalinity and four element alkalinity were 3。12 and 1。76。

(6)Bottom blowing argon stirring can promote the steel slag reaction, improve the desulfurization effect and blowing argon flow the desulfurization effect is better, but high argon gas flow rate will lead to bare steel surface, so as to increase the gas and inclusion in the molten steel, affecting the desulfurization effect。 Therefore, bottom blowing argon flow control in 20 m3 / h, the best desulfurization effect can be obtained。

Key words: furnace refining; LF refining technology; refining slag optimization; analog simulation

目录

第一章 绪论 1

1。1 炉外精炼概况 1

1。1。1 国内炉外精炼技术发展 1

1。1。2 国外精炼技术发展 2

1。1。3 炉外精炼的冶金特点和功能 3

1。2 LF 精炼工艺技术 4

1。2。1 LF 精炼功能 4

1。2。2 LF 精炼工艺流程 6

1。3 本课题研究意义和内容 7

第二章 LF 精炼虚拟仿真操作系统 8

2。1 模拟操作流程 8

2。2 系统界面及功能 9

2。2。1 精炼总览界面 9

2。2。2 钢包系统界面 9

2。2。3 供电系统界面 10

2。2。4 配料系统界面 11

2。2。5 给料系统界面 12

2。2。6 喂丝控制界面 13

2。2。7 底吹控制界面 13

2。2。8 测温取样界面 14

第三章 LF 精炼渣优化研究 16

3。1 精炼渣渣系组成和作用 16

3。2 脱硫模拟试验 18

3。2。1 精炼渣配比 18

3。2。2 模拟结果及分析 18

第四章 吹氩模拟试验 22

4。1 模拟结果及分析 22

结论 24

致谢 25

参考文献 26

第一章 绪论

1。1 炉外精炼概况

炉外精炼也叫“二次精炼”，即将传统的炼钢工艺分为初炼和精炼两步。初炼是 将炉料送入氧化性条件下的炉内进行熔化、脱碳处理。精炼则是在真空、惰性气氛 或还原性气氛的条件下对初炼得到的钢液进行脱氧、脱硫、脱碳、脱气、去夹杂、 控制钢液成分和温度等。

在上世纪 30-40  年代炉外精炼技术就展示了在提高钢材质量、扩大钢材品种等