摘要本文针对低合金钢与中大直径螺柱焊接的需求，开展了焊接工艺和性能测试等研究工作，获得了最佳焊接工艺规范窗口，得到了工艺参数与接头质量的关系。

对ϕ19mm、ϕ22mm的硬质合金钢复合螺柱进行了电弧螺柱焊工艺试验，本文主要探讨焊接电流、焊接时间、阻尼对焊接接头质量的影响，分析焊接接头不规则、熔合不良的成因及其解决措施，实验结果表明：合理调整焊接规范参数和行为能够获得理想的焊接接头，在合适的焊接工艺参数下，焊接过程稳定，焊脚成形美观，接头组织观致密，焊缝没有未熔合、夹渣和裂纹等缺陷，仅少数焊缝中会产生个别点状气孔。86873

毕业论文关键字：硬质合金/钢复合螺柱；螺柱焊；焊接电流；焊接时间；阻尼； 

ABSTRACT    In this paper, the welding process and performance test of low alloy steel and medium large diameter stud welding are carried out, and the optimal welding process specification window is obtained, and the relationship between the process parameters and the quality of the joint is obtained。

On 19 mm, 22 mm of hard alloy clad steel stud the arc stud welding process test, this paper mainly discusses the welding current, welding time, damping on the welding joint quality, analysis of welding irregular, fusion bad causes and measures, experimental results showed that rationally adjust the welding parameters and can obtain ideal welding joints, in the proper welding parameters, the welding process stability and weld legs forming beautiful, dense microstructure view, the weld has no lack of fusion, slag and cracks and other defects, only a handful of weld will produce inpidual punctate stomatal。

Keywords:Hard alloy/steel composite stud;welding current;welding current;welding time; damping;

目录

第一章  绪论 1

1。1 课题研究背景及选题意义 1

1。2 螺柱焊接技术的发展 1

1。2。1 螺柱焊技术的发展历史 1

1。2。2 螺柱焊接技术的发展现状 2

1。2。3 螺柱焊技术的发展趋势 2

1。2。4 螺柱焊待解决的问题 2

1。3 螺柱焊接技术 3

1。3。1 螺柱焊接 3

1。3。2 横焊 3

1。3。3 螺柱焊横焊质量的影响因素 4

1。3。4。 螺柱焊的突出特点 4

1。3。5 螺柱焊的应用 4

1。4 复合螺柱 5

1。5阻尼 5

1。6 本课题主要研究内容 5

第二章  试验材料、设备及方法 7

2。1 试验条件 7

2。1。1 试验材料 7

2。1。2 试验设备 8

2。2 试验方法 9

2。2。1 电弧螺柱焊工艺 9

2。2。2 电弧螺柱焊接头的外观缺陷分析方法 10

2。2。3 复合螺柱横焊宏观金相分析方法 10

2。2。4 复合螺柱横焊接头的微观组织分析方法