摘  要

PVC糊制品在我们的生活中应用十分广泛，但其含有的增塑剂却有一定毒性，危害人们的身心健康。因此我们要制备一种环保增速糊。由2种环保增塑剂制备的DOTP/HDBP增塑糊就是这样的环保增塑糊。本文通过对不同配比的增塑糊的粘度和凝胶化性能进行测试，以及复配增塑剂在PVC中吸收率的测试，研究出当增塑糊中DOTP：HDBP为6:4或5:5时，增塑糊的凝胶化性能达到最好，且增塑糊的粘度很大，DOTP与HDBP按1:1进行复配时，增塑剂能很好的被PVC所吸收。 85285

Abstract

PVC paste products are widely used in our life, but it contains a certain amount of plasticizer toxicity, harm people's physical and mental health。 Therefore, we need to prepare a kind of environmental protection。 The DOTP/HDBP plasticized paste prepared by 2 kinds of environmental friendly plasticizer is the environmental protection plastic paste。 The test of the different ratio of plasticized paste viscosity and gelation properties, and mixed plasticizer absorption test in PVC, developed when plastipaste DOTP:HDBP is 6:4 or 5:5, increase the gelation properties of plasticized paste best and plasticized paste viscosity, DOTP and HDBP was mixed by 1:1, plasticizer can be well absorbed by PVC。

毕业论文关键词：PVC糊制品； 环保增塑糊； 增塑剂； 复配

Keyword：PVC paste；Environmental protection plastic paste；Plasticizer；Formulation 

目    录

目录

一．引言 4

1。1环保增塑糊的源Q于W优H尔J论K文M网WwW.youeRw.com 原文+QQ75201.,8766 研究背景 4

1。2增塑剂的用途与机理 5

1。3传统增塑剂的特点及弊端 6

1。4 环保增塑剂DOTP与HDBP 7

1。5本研究课题的主要意义 8

二．实验部分 8

2。1实验仪器和试剂 8

2。2增塑剂在PVC中的吸收率 9

2。3增塑糊粘度测试 10

2。4凝胶化时间测试 10

三．实验结果与讨论 11

3。1。1增塑剂在PVC中的吸收率 11

3。1。2复配增塑剂在PVC中的吸收率 13

3。2复配增塑糊的粘度随时间的变化 15

3。3复配增塑糊的凝胶化测试 16

四．实验总结 17

参考文献 18

致谢 19

一．引言

1。1环保增塑糊的研究背景

环保增速糊是PVC糊制品的一种，PVC糊树脂与稳定剂、增塑剂等配成糊状进行加工，与悬浮树脂成型加工相比，PVC增速糊能够在室温或接近室温条件下，采用涂刮、模具等手段将增塑糊基本固定后，经受热凝胶化所制得各种制品，具有加工设备价廉，可制成特殊形状，模具简单便宜，发泡容易，制品受热次数少，并可以少量、多品种地生产等优点，因而在人造革、地板革、玩具、浸渍手套、壁纸、油墨、汽车内饰材料等硬制品中得到了广泛应用。

近年来，世界PVC糊树脂工业快速发展，产能、产量均呈现跳跃式增长，其中亚洲地 区尤为显著。2008年世界PVC糊树脂产能约374。2万t/a，占PVC总产能的8。7%；产量约309万t，装置平均开工率约82%。其中中国约占全球总产能的15。0%，占亚洲总产能的64。0%。2008年中国PVC糊树脂产量36万t，约占世界总产量的11。0%，是亚洲地区最大的PVC糊树脂生产国，位居世界第三。2000~2008年我国PVC糊树脂产能、产量年均增速分别为18。7%和16。0%。国外发达国家PVC糊树脂生产企业绝大多数采用乙烯法路线，规模较大。从PVC糊树脂产品品种、牌号来看，各公司根据自身实际情况有一定差别。