摘要本篇文章简要阐述了超高强钢焊接研究现状以及数值模拟的研究现状。通过对超高强钢厚大构件脉冲MIG焊焊接原理及工艺的分析，采用ADINA有限元分析软件建立了不同加载位置、不同数量和不同状态从热源的焊接过程温度场的有限元分析模型，同时通过模拟分析各种从热源模型的焊接过程温度场分布，通过对比分析不同情况下的温度场分布图，得出了从热源施加位置在钢板上表面边缘处时焊件温度场分布比从热源施加在钢板上表面中部时焊件温度场分布更加均匀，从热源施加个数为两个的焊件温度场分布比从热源施加个数为四个的焊件温度场分布更加均匀，相同施加位置条件下，移动式从热源加载下的焊件温度场分布比固定式热源加载下的焊件温度场分布更加均匀。68172

毕业论文关键词   超高强钢  脉冲MIG焊  主从热源  数值模拟

毕业设计说明书（论文）外文摘要

Title Numerical simulation analysis of ultra high strength steel components from the primary heat source  welding process 

Abstract

This article briefly describes the ultra high strength steel welding current research and numerical simulation of the status quo. Through the ultra high strength steel Heavy member pulsed MIG welding principle and process analysis using ADINA finite element analysis software to establish a different loading positions, different amounts and different states of the welding process from the heat source temperature field finite element analysis model, through simulation analysis of various models of the welding process from the heat source temperature distribution through the comparative analysis of different scenarios of temperature distribution, obtained from the heat source is applied to the upper surface of the plate position when the edge of the weldment temperature distribution is more uniform than from the heat source is applied over when the upper surface of the central steel weldment, the number of two from the heat source is applied to the temperature distribution of the weldment is more uniform than four. in the same position , mobile under load from the heat source temperature distribution of weldment is more uniform than the fixed.

Keywords high strength steel  pulsed MIG welding master-slave heat numerical simulation

目录

1  绪论 1

1．1  选题背景及意义 1

1．2  超高强钢焊接方法研究现状 1

1．3  焊接温度场数值模拟的研究现状 2

1．4  本文主要研究内容 3

2  超高强钢厚大构件脉冲MIG焊焊接工艺分析 4

2．1  超高强钢厚大构件脉冲MIG焊焊接特点 4

2．2  超高强钢厚大构件脉冲MIG焊焊接工艺 5

3  超高强钢厚大构件主从热源焊接温度场的有限元模拟 6

3．1  超高强钢厚大构件主从热源焊接过程温度场模型的建立 6

3．2  超高强钢主从热源焊接温度场有限元模拟的结果分析 12

结  论 16

致  谢 17

参 考 文 献 18

1 绪论

1．1  选题背景及意义

针对目前超高强度钢厚大构件在某些领域如军工领域重型车辆上的应用，我国在超高强度钢厚大构件焊接方面也有相应的研究，通过查阅文献[1,2,3,4,5]可知因其高强度、高韧性和抗腐蚀性能而被广泛用于工程机械、电力、压力容器、汽车、航空航天等领域，用于制造承受高应力的重要构件，是制造国防尖端武器的关键材料，具有重要地位，在今天和可预见的未来,它仍将是一种不可替代的关键材料之一。但由于超高强钢的焊接特点及难点，从文献[6]了解到超高强钢焊接时会产生焊接氢致裂纹( 冷裂纹)，焊接时焊接热影响区会软化及其韧性会下降并且焊接时焊接接头会产生疲劳等, 但其中焊接冷裂纹是其中的主要问题。论文网