摘要铜铝接头具有优良的物理性能，广泛应用于各个领域。而钎焊是将铜铝连接 在一起的有效方法，对母材的影响较小。本次实验采用火焰钎焊的焊接方法对铜 铝（纯铜与纯铝、6063 铝合金与纯铜）进行钎焊，使用金相显微镜、差热分析仪、 扫描电镜、电导仪、钳工夹具等实验仪器对铜铝钎焊中的钎料钎剂熔点、焊缝的 金相及缺陷、导电性、力学性能进行了分析。实验结果表明:对铜铝金属进行火焰 钎焊是可行的；钎焊的焊缝与母材的结合良好且母材变形量小；钎焊过程中形成 了金属间化合物，产生了脆性相，导致接头的力学性能较差，但可用来导电。79805

毕业论文关键词：钎焊；铜铝异种金属；焊缝；力学性能

Abstract Aluminum joints have excellent physical properties, widely used in various fields。 While brazing is the effective method in the copper aluminum connecting together, has little effect on the parent material。 This experiment using flame brazing welding method brazing of copper and aluminum, aluminum and copper, 6063 aluminum  and  copper), using metallographic microscope, differential thermal analysis, scanning electron microscopy (SEM), conductivity meter, bench clamp apparatus of copper and aluminum brazing solder flux melting, welding gold phase and defect, conductivity, mechanical properties were analyzed。 The experimental results show that the flame brazing of copper and aluminum metal is feasible; brazing weld and base material with good and parent material and a small amount of deformation; brazing process formed inter metallic compounds, produced the brittle phase, resulting in poor mechanical properties of joints, but can be used to conduct。

Keywords:  Brazing; Dissimilar   metals   of   copper   and   aluminum; Weld; Mechanical property

目 录

第一章 绪论 1

1。1  铜铝异种金属的性能和应用 1

1。1。1 铜、铝金属的物理性能 1

1。1。2 铜、铝的应用 2

1。2  钎焊 2

1。2。1 钎焊的原理 2

1。2。2 钎焊的分类 6

1。2。3 钎焊的应用 7

1。2。4 钎焊的研究现状 8

1。3  铜铝异种金属的焊接 9

1。3。1 铜铝异种金属存在的问题 9

1。3。2 铜铝异种金属的焊接方法 11

1。4  选题意义 13

1。5  本课题的研究内容及方法 13

第二章 实验材料及方法内容 14

2。1  实验材料 14

2。1。1  钎料及 DTA 曲线分析 14

2。1。2  钎剂及 DTA 曲线分析 14

2。1。3 母材 14

2。2  实验设备 15

2。2。1 金相显微镜 15

2。2。2 扫描电镜(SEM) 15

2。2。3 差热分析仪 16

2。3  实验方法