摘要本课题在查阅相关文献及现有设备条件的基础上，结合国内外电弧螺柱焊的相关实 验结果，主要探讨了 Φ22mm 硬质合金（YG6C）/钢（16Mn）复合螺柱螺柱平焊工艺， 通过分析实验结果，对比实验数据，研究了焊接电流、焊接时间等参数对焊接接头质量 的影响。79804

对 Φ22mm 硬质合金（YG6C）/钢（16Mn）复合螺柱螺柱平焊工艺研究结果表明： 在合适的焊接工艺参数下，焊接过程稳定，焊脚成形良好；接头组织致密，气孔、裂纹 等宏观缺陷较少。

毕业论文关键字：焊接电流；焊接时间；螺柱焊；硬质合金

Abstract On the basis of consulting related literatures and existing equipment conditions, this paper mainly discusses the composite stud welding process of 22 mm diameter tungsten carbide(YG6C)/steel(16Mn) by combining with the relevant experimental results of arc-stud welding domestic and overseas, and researching the effects of the parameters such as welding current, welding time on the quality of the welded joint by analyzing the experimental results and comparison  of the  experimental  data。

The results showed that under the proper welding process parameters  the  welding process was stable, good welding feet and pyknotic joint organization were obtained, besides, macroscopic defects such as porosity was lesser。 At the time of welding process parameters was improper,  welding  feet  forming  was bad, and existing  large  amounts  of  porosities。

KeyWords:  welding   current;  Welding  time;  arc stud  welding;   Hard  alloy;

目 录

第一章 绪论 1

1。1  引言 1

1。2  课题研究背景及选题意义 1

1。2。1  课题研究背景 1

1。2。2  选题意义 3

1。3  螺柱焊技术 4

1。3。1  电弧螺柱焊的概念 4

1。3。2  螺柱焊技术的特点及应用 4

1。3。3  螺柱焊接区的保护 5

1。3。4  影响螺柱焊接质量的因素 5

1。3。5  螺柱焊接技术的研究现状及发展趋势 6

1。4  本课题研究的内容 7

第二章 试验材料、设备及方法 9

2。1  试验材料 9

2。1。1  试验所用基体母材 9

2。1。2  硬质合金/钢复合螺柱 9

2。1。3  陶瓷保护圈 9

2。2 焊前准备 10

2。3 实验设备 10

2。4  试验方法 11

2。4。1 硬质合金/钢复合螺柱的钎焊 11

2。4。2  复合螺柱焊接工艺 12

2。4。3  复合螺柱平焊接头外观成形检测 13

2。4。4  复合螺柱平焊接头宏观金相分析 13

2。4。5  复合螺柱平焊接头显微组织分析 13

2。4。6  复合螺柱平焊接头硬度分布测量