摘 要：利用对甲苯异氰酸酯对凹凸棒土进行改性并利用红外、X射线衍射、比表面等对改性前后凹凸棒土进行了表征。结果表明，对甲苯异氰酸酯有效地以化学键的形式结合到凹凸棒土表面，但没有改变凹凸棒土结构。测定了改性后的凹凸棒土对噻虫嗪的吸附能力。实验结果显示：对甲苯异氰酸酯-凹土对噻虫嗪最佳吸附最佳条件为在pH=6的水溶液中，吸附时间1。25 h，0。50 g改性凹土在常温下对噻虫嗪吸附量达96 %。91199

毕业论文关键词：对甲苯异氰酸酯，凹凸棒土，有机改性，噻虫嗪，吸附

Abstract： The attapulgite powders were organically modified using p-tolyl isocyanate。 The raw and modified attapulgite powders were characterized by IR, BET and XRD 。 The results showed that that the main interaction between attapulgite surface and p-toluene isocyanate are chemical bonds and the  crystal structure of attapulgite was unaffected。 Adsorption properties of the modified attapulgite toward pymetrozine were investigated。 The optimal conditions for adsorbing thiamethoxam with the modified attapulgite were obtained: at room temperature, dosage of adsorbent were 0。50 g, pH was 6, adsorption time was 1。25 h, the pymetrozine removal efficiencies reached 96 %。

keyword: p-Tolyl isocyanate, attapulgite powder, organically modify, thiamethoxam, adsorption

目   录

1 引言 4

2 实验部分 4

2。1试剂和仪器 4

2。1。1 试剂 4

2。1。2 仪器 4

2。2 改性凹凸棒土的制备 5

2。2。1凹凸棒土的硝酸处理 5

2。2。2氨基凹土的制备 5

2。2。3改性凹凸棒土的制备 5

2。3 改性凹土对噻虫嗪来自优I尔Y论S文C网WWw.YoueRw.com 加QQ7520~18766 的吸附实验 5

3。结果与讨论 5

3。1改性凹凸棒土的表征 5

3。1。1红外光谱分析 5

3。1。2 X-射线(XRD)分析 8

3。1。3比表面分析 9

3。2 改性凹凸棒土对噻虫嗪吸附测试 10

3。2。1 噻虫嗪标准曲线的确定 10

3。2。2凹凸棒土的加入量对吸附平衡的影响 11

3。2。3时间对吸附平衡的影响 12

3。2。4 温度对吸附平衡的影响 13

3。2。5 pH对吸附平衡的影响 15

结  论 17

参 考 文 献 18

致  谢 19

1 引言 

凹土，是一种具链层状结构的粘土矿物。凹土结构中存在晶格置换[1]，凹土晶体呈针状，纤维状或纤维集合状[2]。1982年江苏盱眙发现广泛分布着凹凸棒土，占全国的73重%。处理后的凹土产物是较为理想的吸附剂、食品加工助剂和食品添加剂，可取代活性炭。它能脱色，除臭除味、消除重金属离子和致癌物质，并具有一定的选择性吸附能力[3]。凹土吸附后可再生，且耗能少，非常有利于环境保护。中国是农业大国，每年有大量的农药废水排入各类水体，污染水源，破坏环境[3-6]。因此选择一种吸附剂去除农田中排出的废水具有非常重要的意义。本文拟用对甲苯异氰酸酯有机改性凹土，测试改性后的产物对废水中噻虫嗪的吸附能力，为今后凹凸棒土处理污水提供依据。