摘 要：本文利用氨基硅烷（KH-912）对凹土（ATP）表面进行改性，制成改性凹土KH-912-ATP，并将其掺杂到聚偏氟乙烯（PVDF）铸膜液中，利用相转化法制备PVDF混合基质超滤膜，考察不同改性剂用量对PVDF膜孔径、微观结构、纯水通量的影响。实验结果表明：改性凹土的添加对膜孔径大小影响不大，纯聚偏氟乙烯膜和改性膜的平均孔径均在20nm左右；随着改性凹土含量的增加，膜指状孔数增加，孔长度变长；不同量的改性凹土掺杂到PVDF膜里后，提高了膜的亲水性，导致膜的纯水通量会增加，且改性凹土掺杂量越多，纯水通量越大。72510

毕业论文关键词：氨基硅烷，凹土，聚偏氟乙烯，相转化法，超滤膜

Abstract: The attapulgite (ATP) was modified with amino-silane coupling agents (γ-aminopropyl-methyldiethoxysilane (KH-912)) by covalent bonding to prepare KH-912-ATP。

The PVDF/ KH-912-ATP hybrid membranes was prepared via a combination of immersion precipitation (IP) and thermally induced phase separation (TIPS) process。 KH-912-ATP was incorporated into PVDF matrix and the influence of modifier amount on membrane structures and properties were investigated in detail。 The result shows that as the increasing dosages of the modifier, the length of finger-like pores got longer, pure water flux (PWF) improved。 The maximum PWF was about 220 L。 m-2 。h-1, nearly two times of the pristine one’s when 7 wt。% of the modifier was added, indicating the improved hydrophilicity and permeability。 

Keywords: Amino silane, attapulgite, polyvinylidene fluoride, phase inversion, ultrafiltration membrane

目   录

1  引言 3

1。1  高分子材料 3

1。2  高分子材料的发展趋势 3

1。3  聚偏氟乙烯的性质及应用 3

1。4  凹土的性质及应用 4

1。5  膜分离技术的优点及应用 6

1。6  研究的主要内容 7

2  实验部分 8

2。1  实验药品和仪器 8

2。2  改性凹土及膜的制备 9

2。3  膜的基本性能表征 10

3  结果与讨论 10

3。1  红外光谱分析 10

3。2  扫描电镜分析 11

3。3  孔径分析 12

3。4  纯水通量 14

结  论 15

参 考 文 献 16

致  谢 18

1  引言

1。1  高分子材料

高分子材料也称为聚合物（或者高聚物）[1,2]，聚合物通常指由很多大分子聚合而成的聚集体，其相对分子质量可高达104~107，但有时高分子也仅仅指一个大分子，这个大分子通常由很多结构单元通过共价键重复键接而成，高分子材料是在高分子化合物基础上由相对分子质量较大的化合物组成的材料。论文网

1。2  高分子材料的发展趋势[3]

1。2。1  改善高分子材料对资源的依赖

当代合成高分子材料主要来自于石油这种化工资源，然而石油的生长又是一个缓慢长期的地质过程，石油资源正面临着日益减少却不能及时再生的现状。因此，有必要寻找其他的资源来代替石油作为新的原料来源。最有效的方法就是研制出新型的高分子材料。