摘 要：本文以乙酸锰、1,2-二（4-吡啶基）乙烯为主要原料，在溶剂DMF中合成了一种新型二维链锰（Ⅱ）配位聚合物[Mn(CH3COO)2(C12H10N2)(H2O)]n，并通过红外光谱图与单晶X-射线衍射分析对其晶体结构作了表征。该配合物属于单斜晶系，空间群为P21/c，晶胞参数分别为a = 1。3959(3) nm, b = 1。7155(4) nm, c = 0。8644(2) nm, β = 107。680(6)°, V = 1。9722(8) nm3, Z = 4, μ(Mo Kα) = 0。693 mm-1, F(000) = 772, R1 = 0。0571和wR2 = 0。1136 [I >2σ(I)]。78196

毕业论文关 键 词：锰（Ⅱ），合成，晶体结构，表征

Abstract:A new 2D chain Mn(II) coordination polymer [Mn(CH3COO)2(C12H10N2)(H2O)]n has beensynthesized in DMF solution with manganous acetate and trans-1,2-Bis(4-pyridyl)ethylene。 The crystal structure of Mn(II) coordination polymer has been characterized by IR and X-ray diffraction single crystal。 Complex crystallizes in the Monoclinicsystem, space group P21/c with cell parameters a = 1。3959(3) nm, b = 1。7155(4) nm, c = 0。8644(2) nm, β = 107。680(6)°, V = 1。9722(8) nm3, Z = 4, μ(Mo Kα) = 0。693 mm-1, F(000) = 772, R1 = 0。0571, wR2 = 0。1136 [I >2σ(I)]。

Keywords：manganese(Ⅱ), synthesis, crystal structure, characterization

目   录

1  前言 3

1。1  锰配合物的研究意义与现状 3

1。2  吡啶类锰配合物的合成与性质 3

2  实验部分 3

2。1  试剂 4

2。2  仪器 4

2。3  [Mn(CH3COO)2(C12H10N2)(H2O)]n的合成 4

3  结果与讨论 4

3。1  [Mn(CH3COO)2(C12H10N2)(H2O)]n红外谱图及数据 4

3。2  [Mn(CH3COO)2(C12H10N2)(H2O)]n配位聚合物的晶体结构 5

结 论 12

参 考 文 献 13

致 谢 14

1前言

配位聚合物一般由金属离子和有机配体通过配位键组装而成，即保持了有机物的特性，又具有无机金属的特性，是一类结构新颖、性能奇特的高分子材料，在吸附、催化、光学、电学和磁学等方面具有重要的潜在应用价值[1-5]。由于它们在理论上的研究价值与所展现的热、力、光、电、磁学性质而可望在信息的存储和传递、光电纤维、照相术、静电印刷术、催化剂、半导体、超导体、陶瓷等领域得到应用[6]，因而近年来得到广泛的关注和研究。论文网

1。1  锰配合物的研究意义与现状

近年来，随着电子工业与计算机工业发展迅速，需要存储和传递的信息不断增加，信息存储技术在不断的发展，这也带动了存储材料研究的热潮，尤其是作为存储材料研究热点之一的分子磁体在高密度信息存储技术方面显现出极大的应用潜力而备受关注[7]。

其中，由于锰的特殊电子构型，导致其配合物在磁性、导电方面具有特殊的功能，成为分子磁体的主要研究对象之一。锰的价电子构型为3d54s2，其核外价电子较多，可以以多种氧化态存在，因而其配位方式也多种多样，能够形成各种结构和性质的配合物，目前已经有人合成出Mn(Ⅱ)、Mn(Ⅲ)、Mn(Ⅳ)以及混合态的配合物[8]。此外，锰离子和配体的结合方式与配位数也具有多样性，最为常见的是六配位和八配位，其配位原子可以是O、N以及Cl-等[9]。