摘  要：聚偏氟乙烯（PVDF）一般是指偏氟乙烯均聚物或偏氟乙烯与其它少许含氟乙烯基单位的共聚物，它兼具氟树脂和通用树脂的特征[1]，除具备良好的耐化学腐蚀性、耐高温性、耐氧化性、耐候性、耐射线腐蚀性能外，还拥有压电性、介电性、热电性等特殊性能[2]。因此在石油化工、电子电气等领域得到了广泛的应用。本文通过静电纺丝技术制备PVDF纳米纤维，在制备过程中考察浓度、距离、推进速度对PVDF纳米纤维形貌的影响。82158

毕业论文关键词：聚偏氟乙烯（PVDF）;静电纺丝法;纳米纤维形态

The preparation of functional PVDF nanofibers and applications

Abstract: Poly (vinylidene fluoride) (PVDF) is a class of polymer with stable physical and chemical property; it combines the characteristics of fluorine resin and general resin。 In addition, it has good resistance to chemical corrosion resistance, high temperature resistance, oxidation resistance, weather ability, rays, corrosion resistance。 Thus, it can be widely used in the petroleum chemical industry, electrical and electronic, and other fields h。 In this article,  we fabricated PVDF nanfibers through the electrostatic spinning technique, and focused the concentration of polymer in the preparation process, distance, velocity influence on PVDF nanofibers morphology。

Key Words: Electrospining; Nanofibers morphology；Poly (vinylidene fluoride) (PVDF)

目    录

摘  要: 1

引  言 1

1实验部分 3

1。1实验仪器与实验试剂 3

1。2 PVDF溶液的配制 3

1。3实验过程 4

1。4测试方法 4

2结果与分析 4

2。1 PVDF纳米材料的扫描电镜分析 4

2。2 浓度对PVDF纳米材料的影响 4

2。3 讨论 6

3结论 7

参考文献 7

致  谢 10

功能性PVDF纳米纤维的制备及应用引言

纳米材料科学从无到有地发展起来，始于20世纪70年代，并逐渐在发展研究中受到众多科技工作者的广泛关注。纳米纤维作为一种新型材料，由于其良好的发展前景近年来受到了研究人员广泛的关注[3]。通常来说在1 nm-100 nm之间的纤维统称为纳米纤维[4]。因为纳米纤维是纳米级的材料，拥有着非常优秀的发展前景，所以在21世纪受到了很多学者、专家的亲睐，而且随着对纳米纤维研究的进行，发掘出了它很多的优点，比如：长径比大，所以其活性和表面能增加[5]。正是因为纳米材料在光学、机械、磁学和电学等方面的这些特殊性质，让纳米技术在环境、信息、能源和生命科学等诸多高新技术产业方面有无限的发展前景。也使得纳米材料逐渐成为了目前世界的科学研究热点[6]。所以在航空航天、生物制药、化工生产、机械制造等诸多方面拥有着非常出色的表现[7]。论文网

正常的聚合物纤维制备方式有溶液纺丝、熔融纺丝、胶体纺丝和液晶纺丝等[8-10]。使用这些传统的方法得到的纤维直径通常为5 um-500 um之间。而高压静电纺丝技能要比以前的方式制得的纤维径直小得多，正常在数纳米到数微米之间，用静电纺丝制备的无纺布，它具有高孔隙率的许多优点、比表面积、大、高纤维的细度、长径比、大[11-13]。是迄今为止制备纳米纤维材料的主要方法[14]。