摘  要：石墨烯是通过一系列操作从石墨中分离的，仅仅只有一层碳原子厚度的二维晶体。由于其特殊的单原子层结构使其具有超高的导电性、高强度、比表面积大、透光性高、导热性极强等特点。常用得到石墨烯的方法有氧化还原法、机械剥离法、化学气相沉积法、外延生长法等。本文通过热还原法制备石墨烯。并对石墨烯的性能表征及应用进行分析与展望。83300

毕业论文关键词：石墨烯；性能表征；制备；氧化还原法

Preparation And Characterization of Graphene

Abstract: Graphene is isolated from graphite by a series of operations, and has only one layer of carbon atoms in thickness of two-dimensional crystals。 Due to the special single atomic layer structure, this makes it has the characteristics of high electrical conductivity, high strength, large surface area, high transmittance, and strong thermal conductivity。 There are many methods preparing graphene oxidation, such as reduction method, mechanical stripping method, chemical vapor deposition, epitaxial growth。 This paper Synthesizes graphene by thermal reduction method, and elaborates performance characterization and application of graphene analysis and prospect。 

Key Words: Graphene; Characterization; Preparation; Oxidation reduction method

目    录

摘  要 1

引  言 1

1 实验部分 3

1。1 仪器与试剂 3

1。2 试验方法 3

2 石墨烯的表征 3

2。1 X-射线粉末衍射分析 3

2。2 红外光谱表征 5

2。3 热重分析 5

2。4 扫描电子显微镜（SEM)表征 6

2。5 拉曼光谱表征 7

2。6 XPS谱图表征 7

3 石墨烯的性能 8

3。1 石墨烯的电学性能 8

3。2 石墨烯的光学性能 8

3。3 石墨烯的机械特性 9

3。4 石墨烯的导热性 9

3。5 石墨烯的比表面积 9

4 石墨烯的应用 10

5 总结与展望 10

5。1 论文总结 10

5。2 展望 10

参考文献 11

致  谢 13

石墨烯的制备及性能表征引  言

2004年，石墨烯第一次在实验室中被发现，就引起了科学界的极大震动，使越来越多的科研工作者投入到石墨烯的研究工作中[1]。石墨烯结构特殊，碳单原子层结构，构成二维蜂窝状并且无限延伸[2]。如下图1所示，正是这种特殊的结构使石墨烯具有优秀的物理化学性质。例如，完美的电学性能、优异的导热性能、超大的比表面积、超高的机械强度、优异的光学性能等。文献综述

图1 石墨烯结构图

目前，随着石墨烯在实际应用中的需要，大量、低成本的获得优质石墨烯具有要大意义[3]。机械剥离法制备石墨烯产量极低，并且得到的尺寸难以控制，只适用于实验室理论获得石墨烯[4]。化学气相沉积法生产石墨烯对技术的要求条件高，得到的产品无法应用于微电子元件上[5]。外延生长发制备石墨烯条件苛刻（高温、高真空）并且得到的石墨烯不易从底衬上分离出来，难以大量的成产石墨烯[6]。热还原法制备石墨烯操作步骤简单，原料易得，并且产量高，在大规模制备生产石墨烯方面具有重要意义[7]。论文网