摘要过共晶铝硅合金因其密度低、强度高、耐磨性优良、尺寸稳定性能良好等优良，广泛应用于航空航天和汽车制造等领域。本实验主要研究热处理温度和时间等具体的工艺参数对含硅量18%的热挤压Al-Si合金棒材组织及其性能的影响。对Al-18wt。%Si合金试样进行不同温度和时间的固溶处理和人工时效热处理后，采用扫描电镜、金相显微镜、XRD衍射仪等仪器观察材料的显微组织，以及万能拉伸试验机、洛氏硬度仪测试其力学性能。86686

    实验结果表明：热挤压Al-18wt。%Si合金棒材最佳固溶处理温度为525℃；适宜的固溶处理保温时间为60min~80min；该种热挤压Al-18wt。%Si合金棒材最佳时效温度为170℃，时效时间为4h。

毕业论文关键词：Al-18wt。%Si合金；固溶处理；人工时效；热挤压。 

Abstract Hypereutectic aluminum-silicon is an important casting alloys,and it has superiority properties like low density,high strength,high wear resistance and low thermal-expansion cofficient and so on。It be widely used in aerospace engineering and automotive manufacture。The experiment mainly studys the effect of the technological parameters of heat treatment temperature，heat treatment time on the microstructure and properties of hot extruded Al-18wtSi 。The solution treatments and artificial aging were performed with Al-18wt。%Si sample at different tempreature and time,the microstructure were concluded through scanning electron microscope ,metallurgical microscopes,XRD diffraction instrument and the properties were concluded through tensile testing machine,Brinell's hardness measurement。

  Experimental results indicate that the best solution treatment temperature of hot extruded Al-18wt。%Si is 525℃ ,the best time of solution treatment of hot extruded Al-18wt。%Si is 60min~80min,the best aging temperature of hot extruded  Al-18wt。%Si is 170℃ and the best aging time of hot extruded Al-18wt。%Si is 4h。

Key word: Al-18wt。%Si ; solution treatment;artificial aging;hot extruded

目 录

第一章 绪论 1

1。1 铝及铝合金的概况 1

1。1。1 铝合金的基本性质 1

1。1。2 铝合金的性能 1

1。1。3 铝合金的分类 2

1。2 铝硅合金的相图分析 4

1。3 铝硅合金热处理特点 5

1。4 硅铝合金组织 5

1。5 铝硅合金性能改善的途径 6

1。5。1 热处理 7

1。5。2 变质处理 7

1。5。3 合金化 7

1。5。4 塑性变形 8

1。6 本课题的研究意义和研究内容 8

1。6。1 研究意义 8

1。6。2 研究内容 9

第二章 实验内容 10

2。1 实验材料与设备 10

2。1。1 实验材料 10

2。1。2实验设备及仪器 10

2。2 实验步骤 11

2。3 实验主要应用装置及使用原理 11

2。3。1 切割机床 11

2。3。2 箱式电阻炉