摘要：本文采用水热法以醋酸锌和硫代硫酸钠为原料，在不同反应温度下合成了立方闪锌矿的ZnS纳米球。对所得的样品利用X射线衍射仪（XRD）进行表征。研究在反应时间相同时，温度对纳米ZnS粒子结晶性能和形貌的影响。结果分析表明在温度100到160 ℃范围内，温度的不断升高，更有利于合成出结晶性好且结晶更加规整的纳米ZnS粒子。而且ZnS晶体的粒子粒径随着温度升高不断增加。84625

毕业论文关键词：水热法；硫化锌纳米球；反应温度；结晶度

Preparation and characterization of ZnS nanomaterials

Abstract: In this paper, zinc acetate and sodium sulfate as raw materials were used as raw materials by hydrothermal method, The ZnS nanospheres sphalerite synthesis at different reaction temperature。 The resulting samples were characterized by X ray diffraction (XRD)。 The effect of temperature on the crystallization behavior and morphology of ZnS particles was studied at the same reaction time。 The results showed that the temperature was increased in the range of 100 to 160 degrees, which is more favorable to the synthesis of nano ZnS particles with good crystallinity and more regular crystallization。 And the particle size of ZnS crystal increases with the increasing of temperature。 

Key Words: Hydro-thermal method; Zinc sulfide nano spheres; Reaction temperature; crystallinity; Degree of crystallinity

目    录

摘  要 1

引  言 1

1实验部分 3

1．1实验仪器与试剂 3

1．2样品制备 3

1．3表征方法 5

2结果与讨论 5

2．1 XRD表征分析 5

3结论 7

参考文献 7

致谢 9

ZnS纳米材料的制备与表征引 言

纳米材料因其特异的内部构成而具备特异的性质，使得纳米材料的相关进展成为时下热点[1]。而其中纳米硫化锌在电子学，光学，生物以及医学等领域拥有巨大的开发价值和应用前途[2-4]。纳米硫化锌属于过渡金属硫化物的一种，同时也是纳米半导体材料、发光材料和化工材料[5-7]。因此，对于纳米尺度硫化锌的合成方法和性能研究具有重要的意义。

由于纳米硫化锌的性能与它自身的形貌和空间结构有着很大的关系，因此不同形貌的二维或三位结构纳米硫化锌不断被合成出来，其形貌包括线状、球状、片状、棒状等[8-12]。如今关于纳米硫化锌的制取方法有很多种，主要有液相法、固相法、气相法、生物法以及多种方法联合合成[13-18]。论文网

气相合成法制取纳米硫化锌粒子有多种优点。气相合成法容易得到球状的、不容易发生团聚、而且粒子分布十分均匀的产品。但是由于气相法反应温度很高，而且对反应设备的要求较高。因为条件的限制和得到的产物转化率并不高，使得气相法无法大型生产化。所以气相法存在一定的局限性。

固相法是在将反应物研磨均匀后，然后混合研磨，使反应物在机械研磨的作用下发生化学反应。固相合成法主要经历四个过程。如果使产物成核速度大于生长，将更加有利于纳米晶体的形成。当产物生长速度大于成核速度时，产物主要以块状晶体的形态存在。因此，通常情况下采取存在少量水的湿固相反应法更加有利于纳米粒子的生成[13]。这种方法有着很多的突出优点：工艺不仅简单产率高、可大型生产化、而且稳点性好可以有效的避免反应发生团聚现象。但这种方法合成的产品纳米颗粒分布并不均匀，粒子结晶不规整。很难实现对产品粒子的大小、形貌的准确控制。所以在对产品颗粒要求较高的合成中，无法普遍应用到实际工厂合成中。