摘要：采用电化学的方法制备了偏钛酸（H2TiO3），以H2TiO3为基底用硼氢化钠还原四氯金酸（HAuCl4。）合成了纳米Au@H2TiO3，研究了碘离子（I-）在修饰电极上的电化学催化作用。实验结果说明，当pH小于9时，I- 先被氧化成碘（I2），再被氧化成碘酸根（IO3-），并且I2 和IO3-还原峰可能被发现；当pH大于9时，I- 直接被氧化成IO3-，而IO3-还原产物是I-。79426

毕业论文关键词：纳米Au，H2TiO3，碘，催化作用

Abstract：In this paper the nano gold doped in H2TiO3 were prepared, and the electrochemical catalysis for iodine at the modified electrode was studied。 It was demonstrated that when the pH is less than 9, the I- at the modified electrode can be oxidized to be I2 and then IO3-, and the reduction peaks of I2 and IO3- at the modified electrode were also found; when the pH is more than 9, the I- is oxidized to be IO3- directly, and the reduction product of IO3- at the modified electrode is I-。

Keywords: nano gold, H2TiO3, iodine, catalysis

目   录

1 前言 3

2  材料与方法 3

2。1  试剂 3

2。2  仪器 3

2。3  修饰电极的制备 4

3  结果与讨论 4

3。1  Au@TiO2的SEM 4

3。2 Au@TiO2的EDS 5

3。3 H2TiO3和Au@H2TiO3的XRD 6

3。4 Au@H2TiO3的UV 7

3。5 Au@H2TiO3的IR 8

3。6 Au@H2TiO3的EIS 8

3。7 pH对I-的CV的影响 9

3。8扫速对I-的CV的影响 12

3。9I-浓度对I-的CV的影响 13

结论 15

参考资料 16

致谢 17

1前言

H2TiO3即水合二氧化钛（TiO2），具有弱酸性。偏钛酸锂（Li2TiO3）中的锂离子和乙酸中的氢离子置换，可以制成H2TiO3[1]，它是纳米TiO2制备的前驱体 [2-4]。

因为纳米Au具有非凡的催化作用，所以近几年来纳米Au及其复合材料被广泛地应用于各个领域[5-6]。考虑到纳米Au和多孔H2TiO3的优势，如果把纳米Au嵌入H2TiO3，将会生成一个有前景的复合物。

碘是一种智能元素，也是人体必须的微量元素之一。碘对人体有着重要的生理作用，它可以促进生物氧化，调节蛋白质的合成与分解，推动糖和脂肪的新陈代谢，调节水盐代谢，增加维他命的吸收，提高酶活性，促进生长发育和维持正常的中枢神经系统结构。但是，过量的碘会导致甲状腺功能亢进。其中，最好又最便宜预防碘缺乏症的方法是摄入适量的加碘食盐，目前这种方法被很多国家使用着。因此，控制碘在食物中的含量和形态是十分重要的、有意义的。文献综述

本实验中，采用纳米Au@H2TiO3修饰的Au电极（GE）作为电化学传感器，研究了碘在修饰电极上的电化学行为。

2  材料与方法

2。1  试剂

碘化钾（KI）及0。1mm钛箔购买于上海国药。0。05μm氧化铝抛光粉，乙醚，乙醇，去离子水。0。5M 硫酸钠（Na2SO4）-0。2M 氟化钠（NaF）水溶液电解液，4。00mg/L HAuCl4●4H2O，0。10M磷酸盐缓冲溶液（PBS）是由0。1mol氯化钠（NaCl）和0。1mol磷酸氢二钠（Na2HPO4）溶解于1000ml的蒸馏水中制成的，所需pH用6M HCl及1M NaOH调节。所有试剂均为分析纯。