摘要：纤维板因化学胶黏剂的使用，导致其对环境污染较为严重，研究绿色无污染的纤维板就成为目前研究的热点。本论文主要研究纤维素酶对秸秆预处理的工艺，以期为绿色纤维板研制提供依据。首先对纤维素酶预处理工艺的单因子进行优化，优化条件为：温度35℃，酶量1。25U/g，时间3h，料液比1:7；进一步进行了SAS响应面优化，优化结果为：温度40℃，酶量0。5U/g、时间1h、料液比1:5，在该条件下，研制的纤维板弯曲强度达到7。12MPa，与未优化相比提高了2。6倍。本论文的研究结果可为无胶纤维板的研制提供理论及技术依据。76757

毕业论文关键词：纤维板，纤维素酶，玉米秸秆，预处理，弯曲强度

Abstract: Due to the use of chemical adhesives, fiber board leads to the serious environmental pollution。Research on green pollution-free fiber board has become the research hot spot。This thesis mainly studies the cellulose enzyme of straw pretreatment process, in order to provide the basis for green fiberboard development。 First of all, we optimizate the single factor of cellulose enzyme pretreatment technology , and the optimization condition is: temperature 35 ℃, enzyme amount 1。25 U/g, time is 3 h, solid-liquid ratio 1:7;Further in the SAS, the optimization results as follows: temperature 40 ℃, enzyme amount 0。5 U/g, time is1 h , solid-liquid ratio 1:5。 In this condition, the development of the fiberboard bending strength is 7。12 MPa。It increaseded 2。6 times compared with not optimized。The results of this paper can provide theory and technical basis for the development of the fiberboard without glue。

Keywords: Fiber board, Cellulase,Corn stover,Pretreatment,The bending strength

目录

1 前言 3

   1。1 纤维板的发展状况 3

1。2 绿色纤维板的研究概况 3

1。2。1 脲醛树脂（UF）制备纤维板生产工艺 3

1。2。2 异氰酸酯胶(MDI)制备纤维板生产工艺 4

1。2。3利用农作物秸秆制造纤维板技术 4

1。2。4不同预处理方法制造纤维板技术 4

1。3纤维素酶的简介 5

1。4研究思路 6

2。材料与试剂 7

2。1 材料 7

2。1。1 原料 7

2。1。2 试剂 7

2。1。3 溶液 7

2。1。4 仪器 7

2。2实验方法 8

2。2。1纤维素酶预处理秸秆的单因素条件研究 8

2。2。2纤维板响应面优化 9

2。2。3纤维板热压方法 9

2。2。4 力学强度测定 9

2。2。5还原糖含量测定方法 9

3。结果与分析 11

3。1不同纤维素酶活对纤维板强度的影响 11

3。2不同反应时间对纤维板的影响 12

3。3不同料液比对纤维板的影响 13

3。4不同pH对纤维板的影响 14