摘   要脱碳是紧固件一种严重的热处理缺陷，其不仅能造成巨大的经济损失，还能对人身安全造成威胁，对钢及制件表面脱碳层深度的测量是紧固件行业品管控制的要点。本文首先介绍了紧固件的生产工艺流程，其次概述了生产高强度螺栓常用的钢材，并阐述了脱碳的相关知识及影响脱碳的因素，最后对脱碳螺栓进行了性能测试以及脱碳层的观察分析。87187

    本文选择有脱碳的高强度螺栓及制造相应螺栓的原材料线材（冷镦前），观察比较未脱碳、原材料线材（冷镦前）脱碳和热处理脱碳的螺栓螺纹金相组织，并螺栓进行硬度测试、拉力测试等性能测试，最后测定原材料线材（冷镦前）及成品螺栓螺纹的脱碳层深度，分析螺纹螺坯脱碳比，总结螺栓原材料线材（冷镦前）允许半脱碳层的深度。

毕业论文关键词：热处理缺陷；高强度螺栓；脱碳层深度；金相组织

abstract Decarburization is fasteners a serious heat treatment defect。 It can not only cause huge economic losses, but also to the personal safety pose a threat to fastener industry quality control points to measure the surface decarburized layer depth of steel and parts。 In this paper, we first introduce the fastener production process, followed by an overview of the production of high strength bolts of commonly used steel, and expounds the decarbonization of decarburization related knowledge and its influence factors, finally the bolts on the decarburization of performance testing and decarburization layer observation analysis。

The decarbonization of high strength bolt and manufacturing bolt corresponding raw material wire Leng Dunqian, observe no decarburization, raw material wire cold heading (before) decarburization and heat treatment decarburization bolt thread microstructure, and bolts of hardness test, tensile test, finally for the determination of the depth of decarburized layer before heading (raw materials) and refined bolts thread, thread screw billet decarburization, summarize the bolt material wire cold heading (before) allows semi decarburized layer depth analysis。

Key words: heat treatment defect; high strength bolt; decarburization layer depth;  microstructure

目  录

第一章 绪论 1

1。1 紧固件研究现状 1

1。2 高强度螺栓的结构特点及生产工艺 2

1。2。1 结构特点 2

1。2。2 生产工艺 3

1。3 高强度螺栓生产用钢 5

1。4 钢材表面的脱碳层 7

1。4。1 钢的脱碳特性 7

1。4。2 脱碳过程影响因素 8

1。5 本文研究的目的和内容 9

第二章 实验材料及方法 11

2。1 实验材料 11

2。2 实验方法 11

2。2。1 试样的制备 11

2。2。2 螺栓金相组织观察 13

2。2。3 脱碳螺栓的硬度测试 15

2。2。4 螺栓抗拉性能测试 16

第三章 实验结果及分析 17

3。1 螺栓脱碳的金相组织 17

3。3 拉力分析