摘要自制的单分散聚苯乙烯微球为内核，硝酸铈为铈源，合成 PS@CeO2 结构， 并在其表面再包裹一层 Fe-ZSM-5 分子筛，然后煅烧除去聚苯乙烯结构，成为中 空的 CeO2@Fe-ZSM-5 核壳结构。对制得样品进行 X 射线衍射和透射电镜表征。 通过改变硝酸铈的用量、前驱液的搅拌时间、晶化时间、晶化方式等条件，研究 对于中空核壳结构的粒度，厚度，包裹程度的影响。68425

毕业论文关键词 核壳分子筛，Fe-ZSM-5，水热法，表征

Title        Synthesis of transition metal hollow Fe-ZSM-5      

Abstract

With homemade monodisperse PS microspheres for the kernel, cerium nitrate as cerium source, synthetic PS@CeO2 structure. and then wrapped in a layer on its surface made of Fe-ZSM-5 zeolite, calcining the template, a hollow of Fe-ZSM-5 @ CeO2 core  - shell structure is formed.Do X-ray diffraction and TEM characterization of the prepared sample. By changing the amount of cerium nitrate, mixing time precursor solution, crystallization time, crystallization conditions, study on the particle size, thickness, and extent of the hollow core-shell structure wrapping.

Keywords core-shell zeolite    Fe-ZSM-5    hydrothermal   characterization

目录

1 引言 1

1.1 课题研究背景与意义 1

1.1.1 NOX 的危害 1

1.1.2 脱销技术 1

1.2 分子筛的发展 1

1.2.1 ZSM-5 分子筛 2

1.2.2 纳米级 ZSM-5 分子筛的合成 2

1.2.3 Fe/ZSM-5 催化剂研究进展及意义 3

1.3 核壳材料 5

1.3.1 核壳材料的概述 5

1.3.2 核壳材料的制备 5

1.3.3 分子筛核壳材料 7

1.3.4 核壳型分子筛的制备方法 8

1.4 中空沸石材料的制备 8

1.4.1 自组装法 9

1.4.2 模板法 9

1.5 课题的研究内容和研究思路 10

1.5.1 课题的研究内容 10

1.5.2 课题的研究思路 10

2 实验部分 11

2.1 实验试剂和主要仪器 11

2.1.1 实验药品 11

2.1.2